It is found that there are two type of thermal stress on window glass in fire: the thermal stress because surface temperature odds and window frame hold in.

通过分析窗玻璃在火灾中的温度分布，发现窗玻璃在火灾条件下产生的热应力有两种：由于玻璃表面温度不均匀产生的热应力和由于窗框约束产生的热应力。

The finite element analysis shows that the maximum thermal stress is in the outside corners of the glass solder. The thermal stress in the edges of glass solder is also high.

通过有限元法对键合热应力进行分析，得到热应力最大值位于玻璃焊料与硅片接触面的外拐角处，其次是玻璃焊料内外边缘处；

The problems of thermal stress acting on the structures of glass curtain-walls are discussed.

探讨了作用于玻璃幕墙结构上的热应力，讨论了它们所产生的效应及分析方法。

Since the surface of glass have many micro-crack, when the thermal stress reach the critical value, thermal breakage occur.

同时玻璃表面存在大量微裂纹，当热应力达到临界值时，在热应力的作用下产生脆性断裂。

There is only a small influence of the bond frame width of glass solder on the thermal stress.

玻璃焊料线宽对热应力影响不大，厚度和键合温度越大热应力越大。